D Standard Test Method for Indentation Hardness of Rigid Plastics by Means of a Barcol This Model fulfills the requirements of ASTM D and B Designation: D – 95 (Reapproved )e1An American National Standard Standard Test Method for Indentation Hardness of Rig. Buy ASTM D TEST METHOD FOR INDENTATION HARDNESS OF RIGID PLASTICS BY MEANS OF A BARCOL IMPRESSOR from.

Author: Nikokasa Dijind
Country: Portugal
Language: English (Spanish)
Genre: Travel
Published (Last): 19 February 2008
Pages: 71
PDF File Size: 9.31 Mb
ePub File Size: 19.36 Mb
ISBN: 354-8-58768-231-7
Downloads: 27085
Price: Free* [*Free Regsitration Required]
Uploader: Yozshushicage

If it does not, loosen the lock-nut and turn the lower plunger guide in or out to obtain a reading. Barcol Hardness is used to determine the hardness of both reinforced and non-reinforced rigid plastics.

Precision and Bias 6 No.

ASTM D – BARCOL HARDNESS

NOTE r2583 surfaces may be more difficult to support. The principles of Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. Inspection Validating the specifications, value and safety of your raw materials, products and assets. Place the Impressor and the material to be tested or the calibration disk on a solidly supported,?

Evaluating how your products and services meet and exceed quality, safety, sustainability and performance standards. NOTE 2—It is recommended that measurements be made with the Model Impressor when values above 90 are obtained with the Model Impressor and that measurements be made with the Model Impressor when values less than 20 are obtained with the Model No.

  FISHERMEN OF CATAN RULES PDF

Assurance Enabling you to identify and mitigate the intrinsic risk in your operations, supply chains and business processes.

Nonhomogeneous Material Reinforced Plastics 30 40 d2853 60 70 Send us a request Need help or have a question? This standard is subject to revision at any time by the responsible technical committee and must be reviewed every? Values below 10 using the Model Impressor are inexact and should not be reported.

Set the legs on the same surface or on solid material of the same thickness, so that the indentor is perpendicular to the surface being tested.

For each material, all the samples were prepared at one source. Auditing Consulting Sourcing Training. NOTE 3—Drift in readings from the maximum may occur in some materials and can be nonlinear with time. Users of this test method should apply the principles outlined in Practice E to generate data speci?

Barcol Hardness ASTM D

Within the range of hardness measured by these Impressors the Model No. Impressions should not d25583 made within 3 mm 1? Send us a request Wilton UK: A superscript epsilon e indicates an editorial change since the last revision or reapproval.

  BOILER OPERATOR HANDBOOK HESELTON PDF

This greater variation may be caused mainly by the difference in hardness between resin and?

Assurance Testing Inspection Certification. Preparation and Operation of Apparatus 8. The specimen is placed under the indentor of the Barcol hardness tester and a uniform pressure is applied to the specimen until the dial indication reaches a maximum. Take care to avoid sliding or scraping while the indentor is in contact with the surface being tested.

Barcol Hardness ASTM D2583

Validating the specifications, value and safety of your raw materials, products and assets. ASTM D e1. If these readings cannot be obtained, subsequent measurements are not valid. Enabling you to identify and mitigate the intrinsic risk in your operations, supply chains and business processes.

Due to copyright restrictions, we are not able to provide copies of standards. Certification Formally confirming that your products and services meet all trusted external and internal d25883. Last previous edition D — Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend.